• 1


SÄKAPHEN® HR 60® Extra G Red is a superior hydrophobic two-component epoxy-based thermosetting coating.

The coating is chemically resistant to all types of water, including brackish, river and sea water as well as deionized water, various substances ranging from acidic to strongly alkaline, inorganic salts and their solutions, fuels and acidic aqueous solutions and concentrated hydrochloric acid.

The surface is hard elastic with hydrophobic properties and prevents caking, fouling and incrustation.

The coating can be applied on-site. Weather-resistant.

The images are for illustration purposes only and may differ from the actual appearance of the products.


Fields of application:

For the coating of blowers, fans and compressors, the corresponding houses, tanks and vessels, piping, spools and prover loops, for the application in water treatment and desalination.

Salt Spray Test: Download PDF here.


HR 60 Extra G Red has been exposed to the athmospheric conditions present near Abqaiq in the Kingdom of Saudi Arabia for 18 months:

  • ØTemperature from 10°C to 44°C with peaks of 55°C
  • 55% average humidity
  • Sandstorms
  • Salty air

Hardness and impact strength of HR 60 Extra G Red were not affected by the exposure. Apart from the superficial matting no further deterioration within the coating can be determined.


SÄKAPHEN® Coating HR 60 Extra G Red - Product Data

Properties - Cold Cured Duroplast Coating
Resin base - Amine cured Epoxy system
Cure Mechanism - Cold Cured Duroplast Coating
Quantity of components - 2
Color - Iron oxide red
Surface - Glossy
pH Range pH 1-13
Wet Film Thickness per layer µm 150
Total dry film thickness µm 400-500
Coverage approx. kg/m²/DFT 1,2 kg / m² / 500µm
Surface Preparation Sa SA2 ½ - SA 3
Surface Profile µm 40 - 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +120°C
Temperature resistance wet (water) °C -20°C to 70°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C 8-24
Chemical Curing days 7-10
Linear Thermal Expansion µm n/a
Pore testing Volts 2000
Pendulum hardness acc. to König 6° sec 133
Shore D Hardness Shore D 84
Adhesion Test N/mm² [MPa] > 20
Salt spray test hours 1250
Impact Strength mm (1 kg) 550
Surface smoothness (Ra) µm Ø 3 readings 0,40
Surface tension mN/m >28 <35
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7x2,0mm on C-Steel with 67,37 w/mK W/mK n/a