• SÄKAPHEN® SÄKALINE 200

  • 1

TWO-COMPONENT, EPOXY-BASED ABRASION-RESISTANT COATING FOR ACIDIC TO STRONGLY ALKALINE MEDIA WITH CERAMIC FILLING. LIGHT GREY, MATT.

SÄKAPHEN® SÄKALINE 200 is a high-quality hydrophobic two-component abrasion-resistant epoxy-based coating, resistant to various substances ranging from slightly sour to alkaline including all types of water, including brackish, river and sea water as well as deionized water with ceramic fillers.

The coating can be applied on-site.

The images are for illustration purposes only and may differ from the actual appearance of the products.

 

Field of application:

 

Ceramic filled epoxy coating for the coating of boilers and other hot water tanks, industrial water and for sewage gas containers in the paper and pulp industry.

   
   
   
   
   
   
   
   

 


SÄKAPHEN® Coating SÄKALINE 200 - Product Data

Properties - Cold Cured Duroplast Coating
Resin base - Amine cured Epoxy system
Cure Mechanism - Cold Cured Duroplast Coating
Quantity of components - 2
Color - Light grey
Surface - Matt
pH Range pH n/a
Wet Film Thickness per layer µm 400 µm
Total dry film thickness µm 1000-2000
Coverage approx. kg/m²/DFT 2,0 kg / m² / 1000µm
Surface Preparation Sa SA2 ½ - SA 3
Surface Profile µm 40 - 60 µm
Temperature resistance dry (dry air oven) °C 10°C - 150°C
Temperature resistance wet (water) °C 10°C - 85°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C 8-48
Chemical Curing days 7-10
Linear Thermal Expansion µm n/a
Pore testing Volts 4000
Pendulum hardness acc. to König 6° sec 174
Shore D Hardness Shore D 84
Adhesion Test N/mm² [MPa] 20,65
Salt spray test hours 15000
Impact Strength mm (1 kg) 1000
Surface smoothness (Ra) µm Ø 3 readings 0,29
Surface tension mN/m >28 <31
Abrasion resistance mg/1000 r. under examination
Crosscut class n/a
Heat conductivity Ø 12,7x2,0mm on C-Steel with 67,37 w/mK W/mK n/a