• SÄKAPHEN® SI 14® E BKW

  • 1

PHENOLIC-BASED HYDROPHOBIC HEATCURED COATING AS TOP COAT FOR SI 14® E FOR STRONGLY ACIDIC TO WEAKLY ALKALINE MEDIA, ESPECIALLY FOR CHLORINATED HYDROCARBONS. CLEAR TOPCOAT ON GREEN, HIGH GLOSS.

SÄKAPHEN® Si 14® E BKW is a high quality hydrophobic phenolic-based thermosetting heat-cured coating as top coat for Si 14® E.

The coating is chemically resistant to organic and inorganic acids, salt solutions, aliphatic and aromatic chlorinated hydrocarbons.

The surface is hard elastic with hydrophobic properties and prevents caking, fouling and incrustation.

The images are for illustration purposes only and may differ from the actual appearance of the products.

 

Fields of application:

 

Filler-free and pigment-free top coat for
SÄKAPHEN® Si 14® E, especially for the use inside tank containers,
vessels and containers carrying chlorinated hydrocarbons.

   
 

 

 

 

 

 

 

 

 

 

 

 

   

 

SÄKAPHEN® Coating Si 14 E BKW - Product Data

Properties - Heat Cured Duroplast
Resin base - Phenolic resin blend
Cure Mechanism - Heat cured
Quantity of components - 1
Color - Klar
Surface - Glossy
pH Range pH 1 - 8
Wet Film Thickness per layer µm 50
Total dry film thickness µm 25-30
Coverage approx. kg/m²/DFT 0,2 kg / m² / 200µm
Surface Preparation Sa SA2 ½ - SA 3
Surface Profile µm 40 - 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 214
Shore D Hardness Shore D 94
Adhesion Test N/mm² [MPa] > 20
Salt spray test hours under examination
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 0,53
Surface tension mN/m > 28 < 35
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7x2,0mm on C-Steel with 67,37 w/mK W/mK n/a