• SÄKAPHEN® TC-Lining

  • 1

HYDROPHOBIC HEAT-CURED COATING, THREE-DIMENSIONAL CROSS-LINKED, CERTIFIED BY BUREAU VERITAS. BASED ON THERMOSETTING POLYMERS FOR STRONGLY ACIDIC TO WEAKLY ALKALINE MEDIA. RED, MATT.

SÄKAPHEN® TC-Lining Grund & Deck is a high-quality, hydrophobic, high build, one-component coating system, consisting of a base coat and a topcoat, chemically based on various thermosetting polymers with three-dimensional cross-linking.

The coating is chemically resistant to various strongly acidic to weakly alkaline media, aliphatic and aromatic chlorinated hydrocarbons, as well as organic and inorganic salt solutions - certified by Bureau Veritas.

The surface is hard-elastic and has hydrophobic properties. With its high dry film thickness of about 400μm, the coating offers long-lasting protection against abrasion, caking and incrustation.

The images are for illustration purposes only and may differ from the actual appearance of the products.

 

Field of application:

  For the coating of various transportation and storage containers, in particular ISO tank containers, but also process vessels, pipework and impellers.
   
   
   
   
   
   
   
   

 

SÄKAPHEN® Coating TC-Lining - Product Data 

Properties - Heat Cured Duroplast Coating
Resin base - Duroplastic resin blend
Cure Mechanism - Heat cured
Quantity of components - 1
Color - Red (Top coat)
Surface - Satin finished
pH Range pH 1 - 13
Wet Film Thickness per layer µm 100
Total dry film thickness µm 400 - 450
Coverage approx. kg/m²/DFT 0,5 kg / m² / 150µm
Surface Preparation Sa Top coat to be applied on SÄKAPHEN® TC Lining
Surface Profile µm Top coat to be applied on SÄKAPHEN® TC Lining
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 195
Shore D Hardness Shore D 93
Adhesion Test N/mm² [MPa] >30
Salt spray test hours n/a
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings <1
Surface tension mN/m <28
Abrasion resistance mg/1000 r. under examination
Crosscut class 1
Heat conductivity Ø 12,7x2,0mm on C-Steel with 67,37 w/mK W/mK n/a